ARMOR SHIELD
PRODUCT DATA SHEET
RUST PREVENTIVE COMPOUND

P1200 Series Epoxy

PRODUCT CODEARMOREX P1200 SERIES EPOXY
END USEDIRECT-TO-METAL (DTM) EPOXY
RESIN TYPEMODIFIED POLYAMIDE CURED EPOXY
SOLVENT TYPEAROMATIC, KETONE AND ALCOHOL SOLVENTS
VISCOSITYP1200 BASE: 40-45" #2 ZAHN *
C600 CATALYST: 120" #3 ZAHN *
WEIGHT/GALLON9.3 ± 0.2 LBS/GALLON MIXED
WEIGHT % SOLIDS71% ± 2% MIXED *
VOLUME% SOLIDS61% ± 2% MIXED *
SUBSTRATESTEEL
PRETREAT & CLEANSSPC-SP-1, SP-2, SP-3, SP-6 OR SP-10
WET FILM8 - 12 MILS PER COAT *
DRY FILM5 - 7 MILS PER COAT *
FLASH POINTLESS THAN 100°F
GLOSS 60°SPECIFIED BY CUSTOMER. EPOXIES CHALK AND FADE ON PROLONGED EXPOSURE TO SUNLIGHT.
THINNER RATIOTHIN UP TO 10% PER GALLON WITH RA70 REDUCER AS NECESSARY TO SPRAY. IN HOT WEATHER (OVER 80°F) USE RA80 REDUCER.
MIX RATIO3:1 BY VOLUME (P1200 BASE: C600 CATALYST)
P1200 CLEAR HAS A MIX RATIO OF 2:1 BY VOLUME
POTLIFE4 HOURS AT 77°F WHEN MIXED. SHORTER AT HIGHER TEMPERATURES.
DRY TIMETACK FREE: 2 HOURS AT 77°F *
HARD: OVERNIGHT *
CURED: 7-10 DAYS @ 77°F & 50% RELATIVE HUMIDITY *
V.O.C.2.73 LBS/GALLON *
CHARACTERISTICSDIRECT-TO-METAL (DTM) EPOXY WITH EXCELLENT CORROSION RESISTANCE AND CHEMICAL RESISTANCE.
* TYPICAL VALUES, VARY WITH COLOR OR CUSTOMER REQUIREMENTS.

The technical data and suggestions for use contained herein are correct to the best of our knowledge, and offered in good faith. The statements of this website do not constitute a warranty, whether expressed, or implied as to the product performance. Watson can guarantee this product to conform to our standards of quality, and our liability, if any shall be limited to replacement of defective materials. Any or all technical information is subject to change without notice. SEE THE PRODUCT MATERIAL SAFETY DATA SHEET (MSDS) AND LABEL WARNINGS FOR ADDITIONAL SAFETY INFORMATION.